Study on Mechanical Property Variation of EPDM Sealing Materials for GIS Equipment Before and After Aging

WANG Xinxin; HE Cheng; CHEN Jun; ZHAO Puzhi; WEI Shang

doi:10.13296/j.1001-1609.hva.2024.08.013

您当前的位置：

首页 >

文章列表页 >

Study on Mechanical Property Variation of EPDM Sealing Materials for GIS Equipment Before and After Aging

Research & Analysis | 更新时间：2025-04-26

- Study on Mechanical Property Variation of EPDM Sealing Materials for GIS Equipment Before and After Aging
- High Voltage Apparatus Vol. 60, Issue 8, Pages: 106-112(2024)
- 作者机构：
  
  1.国网新疆电力有限公司电力科学研究院，乌鲁木齐　 830011
  2.国网新疆电力有限公司，乌鲁木齐　 830000
- 作者简介：
- 基金信息：
- DOI：10.13296/j.1001-1609.hva.2024.08.013
  CLC：
- Received：18 February 2024，
  
  Revised：14 April 2024，
  
  Published：16 August 2024
- 稿件说明：
移动端阅览
WANG Xinxin, HE Cheng, CHEN Jun, et al. Study on Mechanical Property Variation of EPDM Sealing Materials for GIS Equipment Before and After Aging[J]. High voltage apparatus, 2024, 60(8): 106-112.
DOI：

WANG Xinxin, HE Cheng, CHEN Jun, et al. Study on Mechanical Property Variation of EPDM Sealing Materials for GIS Equipment Before and After Aging[J]. High voltage apparatus, 2024, 60(8): 106-112. DOI： 10.13296/j.1001-1609.hva.2024.08.013.

摘要

GIS设备用三元乙丙（EPDM）橡胶密封材料长期使用会出现老化现象，严重的还会使密封失效进而造成严重的事故。因此文中采用热氧老化的方法同时研究了密封圈与密封条两种不同形态的EPDM橡胶样品于老化前后的力学性能变化，为EPDM在GIS设备中长期应用提供指导。结果表明，邵氏硬度会随着老化时间的增加而逐渐变大，拉伸强度会先增大后减小，而断裂伸长率则会一直减小。将密封圈和密封条的性能作对比，发现密封圈和密封条的性能变化趋势相同，但在变化过程中，密封条的邵氏硬度、拉伸强度和断裂伸长率均大于密封圈。

Abstract

The long-term use of EPDM rubber sealing material for GIS equipment will occur aging phenomenon and will

in case of serious condition

lead to the sealing out of function as well as cause serious accident. Therefore

the thermal oxygen aging method is used in this paper to study the mechanical property variation of such two forms of EPDM rubber samples as sealing ring and sealing strip before and after aging

so to provide guidance for the long-term application of EPDM in GIS equipment. The results show that the Shore hardness will gradually increase with the increase of aging time

the tensile strength will increase firstly and then decrease

but the breakage elongation will always decrease. It is found by comparing the performance of the sealing ring and the sealing strip that the performance variation of the sealing ring and the sealing strip has the same trend

but in the process of the variation

the Shore hardness

tensile strength and breakage elongation of the sealing strip are greater than those of the sealing ring.

关键词

Keywords

references

Views

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

Method on Distinguishing Aging and Deterioration Condition of Insulation and Semi-conductive Materials via Channel Characteristics of Medium Voltage Cable

ANALYSIS ON THE EVALUATION METHOD OF AGING FOR COMPOSITE INSULATORS

Comparison and Analysis of Physical Properties among EPDM,NBR and CR O-Rings Used in Gas Insulating Switch

Study on Aging Characteristics of Insulation in Inverter-fed Traction Motor Based on Dielectric Loss

Aging Character Analysis of Composite Insulators

Related Author

CHEN Jie

LIU Jian

HU Libin

WANG Yuli

TAN Xiao

CAO Jingying

ZHANG Wei

LI Chenying

Related Institution

Wuhan Branch of China Electric Power Research Institute Co., Ltd.

State Grid Jiangsu Electric Power Co., Ltd. Electric Power Research Institute

湖北武汉430074

上海200122

Wuhan High Voltage Research Institute

⁰