Effect of Surface Electrical Tracking of Ethylene Propylene Rubber on Polarization-depolarization Current

FENG Chen; LEI Zhipeng; REN Hongqiu; SONG Jiancheng; TIAN Muqin

doi:10.13296/j.1001-1609.hva.2017.10.023

您当前的位置：

首页 >

文章列表页 >

Effect of Surface Electrical Tracking of Ethylene Propylene Rubber on Polarization-depolarization Current

更新时间：2025-04-26

- Effect of Surface Electrical Tracking of Ethylene Propylene Rubber on Polarization-depolarization Current
- High VoltageApparatus Vol. 53, Issue 10, Pages: 136-141(2017)
- 作者机构：
  
  太原理工大学电气与动力工程学院煤矿电气设备与智能控制山西省重点实验室
- 作者简介：
- 基金信息：
- DOI：10.13296/j.1001-1609.hva.2017.10.023
  CLC： TM215.2
- Published：2017
- 稿件说明：
移动端阅览
[1]冯晨,雷志鹏,任鸿秋,宋建成,田慕琴.乙丙橡胶表面电痕腐蚀对极化——去极化电流的影响[J].高压电器,2017,53(10):136-141.

FENG Chen, LEI Zhipeng, REN Hongqiu, et al. Effect of Surface Electrical Tracking of Ethylene Propylene Rubber on Polarization-depolarization Current[J]. High voltageapparatus, 2017, 53(10): 136-141.
[1]冯晨,雷志鹏,任鸿秋,宋建成,田慕琴.乙丙橡胶表面电痕腐蚀对极化——去极化电流的影响[J].高压电器,2017,53(10):136-141. DOI： 10.13296/j.1001-1609.hva.2017.10.023.

FENG Chen, LEI Zhipeng, REN Hongqiu, et al. Effect of Surface Electrical Tracking of Ethylene Propylene Rubber on Polarization-depolarization Current[J]. High voltageapparatus, 2017, 53(10): 136-141. DOI： 10.13296/j.1001-1609.hva.2017.10.023.

摘要

电痕是引起绝缘表面劣化的主要原因之一。针对矿用乙丙橡胶电缆绝缘表面电痕腐蚀问题

文中以不同电痕发展阶段的乙丙橡胶试样为研究对象

试验测量并分析了乙丙橡胶表面电痕腐蚀程度与极化—去极化电流之间的关系

提取了去极化初始电流值、电流衰减稳定值和凹点出现时间3个特征量。对比不同电痕腐蚀程度试样的极化—去极化电流曲线及其特征量发现:在去极化初始阶段

初始电流值、放电速率和去极化电流衰减稳定时刻的电流值与乙丙橡胶表面电痕损伤程度密切相关;随着测量时间的延长

去极化电流曲线上出现凹点

该凹点出现时间与表面电痕腐蚀程度相关。研究结果证明

使用极化去极化电流方法可以对乙丙橡胶的表面电痕腐蚀程度进行有效评估。

Abstract

Electrical tracking is one of the main reasons for the deterioration of insulation surface.According to the problem of the surface electrical tracking erosion of insulation using in the high-voltage mining cables

the ethylene propylene rubber samples with different electrical tracking development stage are selected in the paper.The relationship between the surface electrical tracking erosion degree of ethylene propylene rubber and polarization-depolarization current is analyzed.Characteristic parameters

which include the initial value of depolarization current

the static value of current attenuation and the time of concave point

are extracted from the depolarization current curves.Comparing the depolarization curves of surface electrical tracking erosion degree of different samples and its characteristic parameters

it has been found that the initial value of depolarization current

the static value of current attenuation and the time of concave point are closely related to the electrical tracking development stage.The concave point can be observed with the increase of measuring time

which relates to the degree of surface electrical tracking erosion.Research results demonstrate that the severity degree of electrical tracking erosion can be discriminated with polarization-depolarization current.

关键词

Keywords

references

Views

104

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

Study on Dielectric Spectroscopy of EPR for Cable Insulation Under Mechanical and Thermal Stresses

Time-domain Analysis of Dielectric Response in Oil-paper Insulation Using Extended Debye Model

Characteristic Parameters Identification of Supercapacitor Based on Improved Least Square Method

Extended Debye Equivalent Circuit Parameter Identification Based on Polarization Current

Debye Parameter Identification Method of Oil-paper Insulation Based on Depolarization Current Prony Algorithm Fitting

Related Author

LEI Zhipeng

LIU Zhaogui

LIU Yang

WANG Siyu

HAN Kunying

SHI Zhijie

WANG Ye

LI Xian-lang

Related Institution

Shanxi Key Laboratory of Mining Electrical Equipment and Intelligent Control, National & Provincial Joint Engineering Laboratory of Mining Intelligent Electrical Apparatus Technology, Taiyuan University of Technology

School of Electrical Engineering, Southwest Jiaotong University

College of Electronic Engineering,Dongguan University of Technology

College of Electronic and Information Engineering,Tongji University

College of Electrical Engineering and Automation,Fuzhou University

⁰