Analysis and Suggestions on String Breakage Failure of Composite Insulator of Overhead Transmission Line in Hunan Power Grid

CHAO Yafeng; WAN Tao; ZHANG Liu; WANG Cheng; YANG Hongjun; WANG Feng; MA Liming

doi:10.13296/j.1001-1609.hva.2021.08.028

您当前的位置：

首页 >

文章列表页 >

Analysis and Suggestions on String Breakage Failure of Composite Insulator of Overhead Transmission Line in Hunan Power Grid

更新时间：2025-04-26

- Analysis and Suggestions on String Breakage Failure of Composite Insulator of Overhead Transmission Line in Hunan Power Grid
- High VoltageApparatus Vol. 57, Issue 8, Pages: 209-215(2021)
- 作者机构：
  
  1. 国网湖南省电力有限公司电力科学研究院
  2. 襄阳国网合成绝缘子有限责任公司
- 作者简介：
- 基金信息：
- DOI：10.13296/j.1001-1609.hva.2021.08.028
  CLC： TM75;TM216
- Published：2021
- 稿件说明：
移动端阅览
CHAO Yafeng, WAN Tao, ZHANG Liu, et al. Analysis and Suggestions on String Breakage Failure of Composite Insulator of Overhead Transmission Line in Hunan Power Grid[J]. High voltageapparatus, 2021, 57(8): 209-215.
DOI：

CHAO Yafeng, WAN Tao, ZHANG Liu, et al. Analysis and Suggestions on String Breakage Failure of Composite Insulator of Overhead Transmission Line in Hunan Power Grid[J]. High voltageapparatus, 2021, 57(8): 209-215. DOI： 10.13296/j.1001-1609.hva.2021.08.028.

摘要

文中针对湖南电网近10年复合绝缘子掉线问题

对掉线案例进行了统计分析

发现500 k V线路掉线概率更大

7次掉线有6次本体损伤和1次设计不合理共两种类型

其中本体损伤有2次为芯棒脆断、4次为芯棒酥断。选取10支样品在实验室开展机械、电气试验

机械破坏负荷、耐漏电起痕、芯棒耐酸试验、剖检试验等均未检出同批次样品不合格情况。提出了复合绝缘子抽检试验项目优化建议

针对掉线重灾区的超高压线路复合绝缘子推荐了入网检测关键项目

同时针对复合绝缘子专项巡视提出了可操作的具体建议。

Abstract

In view of string breakage problem of composite insulator in Hunan Power Grid of last 10 years in

the string breakage case is statistically analyzed

finding that the string breakage probability of 500 k V line is higher.There are two types of breakages out of the 7 times

one type is 6 times of insulator proper damage and the other type is 1 time of unreasonable design.In the former type 2 times are core brittle fracture and 4 times are core bar brittle breakage.10 pieces of samples are selected for mechanical and electrical tests in the laboratory.The same batch of samples were not found to be unqualified by mechanical damage load

anti-leakage tracking

acid resistance test of core bar and autopsy test and so on.The optimization suggestion of sampling test items of the composite insulator is proposed.The key items of access detection of composite insulator of EHV transmission lines in severe string breakage area is recommended and

at the time

specific operational suggestion for the special patrol inspection of composite insulator is proposed.

关键词

Keywords

references

Views

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

Seismic Response and Impact Analysis of UHV Composite Double-pillar Equipment with Tubular-busbar Coupling

Thermal Aging Characteristics Analysis of HTV Silicone Rubber Composite Insulator Shed

Study on Hydrophobicity Diagnosis Method of Composite Insulator Based on Lightweight Convolution Neural Network

Study on Distribution of Decay-like Fracture of Composite Insulator

Parameter Analysis for Breaking Circuit with Artificial Current Zero

Related Author

LI Qiang

ZHANG Changhong

YU Rongxing

CHEN Chaoquan

LYU Li

XIA Lingzhi

HUANG Hongfei

GUO Kaihang

Related Institution

CSG Extra High Voltage Power Transmission Company, Dali Bureau

Extra High Voltage Power Transmission Company Electric Power Research Institute

China Southern Power Grid Co., Ltd.

State Grid Anhui Electric Power Research Institute

Beijing International S & T Cooperation Base for Plasma Science and Energy Conversion, Institute of Electrical Engineering Chinese Academy of Sciences

⁰